[1]刘少胡,张益维,管锋,等.含缺陷连续管冲蚀规律研究[J].中国安全生产科学技术,2016,12(10):92-95.[doi:10.11731/j.issn.1673-193x.2016.10.015]
 LIU Shaohu,ZHANG Yiwei,GUAN Feng,et al.Study on erosion laws of coiled tubing containing defect[J].JOURNAL OF SAFETY SCIENCE AND TECHNOLOGY,2016,12(10):92-95.[doi:10.11731/j.issn.1673-193x.2016.10.015]
点击复制

含缺陷连续管冲蚀规律研究
分享到:

《中国安全生产科学技术》[ISSN:1673-193X/CN:11-5335/TB]

卷:
12
期数:
2016年10期
页码:
92-95
栏目:
现代职业安全卫生管理与技术
出版日期:
2016-10-30

文章信息/Info

Title:
Study on erosion laws of coiled tubing containing defect
作者:
刘少胡1张益维2管锋1马卫国1魏世忠1
(1.长江大学 机械工程学院,湖北 荆州 434023; 2. 西南石油大学 机电工程学院,四川 成都 610500)
Author(s):
LIU Shaohu1 ZHANG Yiwei2 GUAN Feng1 MA Weiguo1 WEI Shizhong1
1. School of Mechanical Engineering, Yangtze University, Jingzhou Hubei 434023, China; 2. School of Mechatronic Engineering, Southwest Petroleum University, Chengdu Sichuan 610500, China
关键词:
连续管内壁已有缺陷冲蚀水力压裂
Keywords:
coiled tubing internal wall existing defect erosion hydraulic fracturing
分类号:
X937
DOI:
10.11731/j.issn.1673-193x.2016.10.015
文献标志码:
A
摘要:
针对内壁含缺陷的连续管冲蚀磨损严重、易失效的问题,基于冲蚀理论和液-固两相流,建立了含缺陷连续管内 壁冲蚀模型。利用Grant和Tabakoff模型求解砂砾冲蚀速率,借助实验数据验证了CFD数值模型。利用该模型研究了连续 管内壁周向均布缺陷数量及缺陷形状参数(深度、长度和宽度)对连续管内壁含缺陷时的冲蚀影响。研究表明:完整连 续管与含1个缺陷时对比,最大冲蚀率增加了4.5倍。对于深度或宽度较小的缺陷,冲蚀更为严重,缺陷会在冲蚀作用下 迅速加深或变宽,增速下降较快。含大长度缺陷连续管在压裂中会被加速损坏。
Abstract:
The erosion of coiled tubing(CT) containing defects in internal wall is serious, and the CT is easy to fail. Based on the erosion theory and fluid & solid two-phase flow dynamics, an erosion model of internal wall for CT containing defects was established. The Grant and Tabakoff models were applied to calculate the erosion rate of gravel, and the CFD numerical model was verified with the experimental data. The erosion influence of the number of defects with circumferential uniform distribution in internal wall of CT and the shape parameters of defects such as depth, length and width on CT containing defects in internal wall was studied by the model. The results showed that the maximum erosion rate of CT containing one defect increases 4.5 times compared with the complete CT. The erosion is more serious for the defects with smaller depth or width, and the defects deepen or widen rapidly under the effect of erosion, with a faster drop of growth rate. The damage of CT containing defects with large length will be accelerated in the fracturing.

参考文献/References:

[1]Feng Guan, Menglan Duan, Weiguo Ma, et al. An experimental study of mechanical behavior of coiled tubing in pipelines [J]. Applied Ocean Research, 2014, 44:13-19.
[2]W.G. Gavin, Fracturing through coiled tubing-recent developments and case histories[R], SPE 60690, in: SPE/ICoTA Conference Proceedings, Houston, TX, April, 2000.
[3]祝效华,刘少胡,童华.气体钻井钻杆冲蚀规律研究[J]. 石油学报,2010,31(6):1013-1017. ZHU Xiaohua,LIU Shaohu,TONG Hua. A study on the drill pipe erosion law in gas drilling [J]. Acta Petrolei Sinica ,2010,31(6): 1013-1017.
[4]郑华林,张益维,刘少胡. 水力压裂冲蚀磨损对连续管剩余寿命影响研究[J]. 中国安全生产科学技术, 2016,12(7): 5-10. ZHENG Hualin, ZHANG Yiwei, LIU Shaohu. Study on effect of erosion wear to residual life of coiled tubing for hydraulic fracturing[J]. Journal of Safety Science and Technology, 2016,12(7): 5-10.
[5]李诗卓,董祥林.材料的冲蚀磨损与微动磨损[M].北京:机械工业出版社,1987:17-33.
[6]陈兆雄,吴明,程猛猛,等. 辽河油田埋地集输管道剩余寿命的预测[J]. 材料保护,2014,47(5):34-36. CHEN Zhaoxiong, WU Ming, CHENG Mengmeng, et al. Residual life prediction of buried gathering pipelines at Liaohe oilfield [J]. Materials Protection, 2014,47(5):34-36.
[7]刘少胡,冯定,刘旭辉. 连续管管体失效机理及预防措施研究 [J]. 长江大学学报 (自然科学版),2015,12 (19):42-46. LIU Shaohu,FENG Ding,LIU Xiuhui. Failure mechanism and preventive measures for coiled tubing body [J ], Journal of Yangtze University (Natural Science Edit),2015,12(19):42-46.
[8]毕宗岳,张鹏,井晓天,等. 连续油管在川东气田的腐蚀行为研究[J]. 焊管2011,34(4):26-28. BI Zongyue, ZHANG Peng, JING Xiaotian, et al.. Study on corrosion behavior of coiled tubing in east Sichuan gas field [J]. Welded Pipe and Tube,2011,34(4):26-28.
[9]Zhanke Liu, Andrew Zheng, Oscar O. Rivas Diaz,et al.. A Novel Fatigue Assessment of CT with Defects Based on Magnetic Flux Leakage [R]. SPE-173664-MS. 2015.
[10]Steven Tipton, Ed Smalley, Don VanArnam. Influence of a Straightener on Coiled Tubing Fatigue [R ]. SPE-154057-MS, 2012.
[11]叶彬,朱做涛,穆志韬. 铝合金材料腐蚀形貌及裂纹扩展分析[J]. 装备环境程,2011,8(4):54-58. YE Bin, ZHU Zuotao, MU Zhitao. Corrosion morphology and crack growth analysis of aluminum alloy material [J]. Equipment Environmental Engineering,2011,8(4):54-58.
[12]刘少胡, 郑华林. 基于气固两相流的气体钻井套管冲蚀数值模拟研究 [J]. 热加工工艺,2014,43(12): 96-98. LIU Shaohu, ZHENG Hualin. Numerical simulation on casing erosion wear based on gas-cuttings flow in gas drilling [J]. Hot Working Technology,2014,43(12):96-98.
[13]L. L. Baxter and P. J. Smith. Turbulent Dispersion of Particles[J]. The STP Model Energy & Fuels, 1993, 7: 852-859.
[14]Netaji Ravikiran Kesana.Erosion in multiphase pseudo slug flow with emphasis on sand sampling and pseudo slug characteristics [D].Tulsa:The University of Tulsa,2013.
[15]Subhash N. Shah,Samyak Jain. Coiled tubing erosion during hydraulic fracturing slurry flow[J]. Wear,2008,264(3): 279-290.

相似文献/References:

[1]吴晗,刘少胡,刘旭辉,等.焊肉位置对连续管冲蚀磨损规律研究[J].中国安全生产科学技术,2017,13(2):138.[doi:10.11731/j.issn.1673-193x.2017.02.024]
 WU Han,LIU Shaohu,LIU Xuhui,et al.Study on erosion wear laws of coiled tubing affected by weldment position[J].JOURNAL OF SAFETY SCIENCE AND TECHNOLOGY,2017,13(10):138.[doi:10.11731/j.issn.1673-193x.2017.02.024]
[2]刘少胡,李思行,冯定,等.连续管钻塞水平段铁屑运移机理研究[J].中国安全生产科学技术,2017,13(6):58.[doi:10.11731/j.issn.1673-193x.2017.06.009]
 LIU Shaohu,LI Sixing,FENG Ding,et al.Study on migration mechanism of iron filings in horizontal section during drilling plug with coiled tubing[J].JOURNAL OF SAFETY SCIENCE AND TECHNOLOGY,2017,13(10):58.[doi:10.11731/j.issn.1673-193x.2017.06.009]
[3]郑华林,张益维,刘少胡.水力压裂冲蚀磨损对连续管剩余寿命影响研究[J].中国安全生产科学技术,2016,12(7):110.[doi:10.11731/j.issn.1673-193x.2016.07.020]
 ZHENG Hualin,ZHANG Yiwei,LIU Shaohu.Study on effect of erosion wear to residual life of coiled tubing for hydraulic fracturing[J].JOURNAL OF SAFETY SCIENCE AND TECHNOLOGY,2016,12(10):110.[doi:10.11731/j.issn.1673-193x.2016.07.020]

备注/Memo

备注/Memo:
国家自然科学基金项目(51604039);湖北省教育厅科学技术研究计划青年人才项目(Q20161310);长江 大学青年基金项目(2015cqn44);长江大学油气钻完井工具研究中心资助项目(OGT201502)联合资
更新日期/Last Update: 2016-11-30