WNS型燃气蒸汽锅炉管板（管口）泄漏原因分析
XUEFeng,LU Zhong-ming,WANG Lian.Analysis on leakage reasons of tube sheet (tube mouth) on WNS gas steam boiler[J].JOURNAL OF SAFETY SCIENCE AND TECHNOLOGY,2015,11(9):191-196.[doi:10.11731/j.issn.1673-193x.2015.09.030]
《中国安全生产科学技术》[ISSN:1673-193X/CN:11-5335/TB]
- 卷:
- 11
- 期数:
- 2015年9期
- 页码:
- 191-196
- 栏目:
- 职业安全卫生管理与技术
- 出版日期:
- 2015-09-30
文章信息/Info
- Title:
- Analysis on leakage reasons of tube sheet (tube mouth) on WNS gas steam boiler
- Keywords:
- boiler; smoke tube; leakage
- 分类号:
- X933.2
- 文献标志码:
- A
- 摘要:
- 某医院有两台WNS10-1.25-Y/Q燃气锅炉,连续发生多次回燃室前管板烟管管口泄漏故障,分析了缺陷产生的原因，并提出了解决方法。在长期交变热应力作用下，烟管管口角焊缝熔合线区域产生内部微裂纹，微裂纹在交变热应力（断口分析的形貌为韧窝）的作用下逐步扩展，形成内部宏观（金相检验时发现了多条内部裂纹，且裂纹走向是平行于烟管轴向的方向），裂纹沿着轴向向烟管前后端扩展，最终扩展到管端，并穿透管壁，导致锅炉汽水从裂口泄漏。
- Abstract:
- There exists 2 WNS10-1.25-Y/Q gas boilers in a certain hospital, and the leakage faults have occurred in the tube mouth of smoke tube on front tube sheet of reversal chamber for several times continuously. The reasons of defects were analyzed, and the solving methods were put forward. Under the long term action of tremendous thermal stress, the internal micro cracks came into being in the fillet weld junction region on tube mouth of smoke tube. The micro cracks expanded gradually under the action of tremendous thermal stress (the morphology of fracture analysis is dimple), and formed the internal macro (multiple internal cracks were found in metallographic examination, and the crack path was parallel to the axial direction of smoke tube). The cracks expanded to the front end and back end of smoke tube, and finally reached the tube end, then penetrated the wall of tube, resulting in leakage of steam-water from the gap.
参考文献/References:
［1］席代国，王彬.WNS型锅壳式锅炉烟管管端、管孔裂纹漏水现象的分析［J］.工业锅炉，2014（4）：60-64
XI Dai-guo,WANG Bin. Cause analysis of WNS shell boiler cracks and leakage at tube ends of the fire tube［J］. Industrial Boiler,2014(4)：60-62
［2］纪丽伟.一起锅炉管板管孔及烟管管口裂纹的原因分析与改进［J］.工业锅炉,2009(6):49-50,53
JI Li-wei.The cause analysis of crack on tube plate and tube of one boiler［J］.Industrial Boiler,2009(6):49-50,53
［3］刘小东，祖双福，林兴涛.燃油气中心回燃式锅炉前管板管端裂纹原因分析与改造方案［J］.工业锅炉,2014(6):47-50
LIU Xiao-dong,ZU Shuang-fu,LIN Xing-tao.Cause analysis and retrofit scheme of the front tube crack of gas and oil fired central reverse flame boiler［J］. Industrial Boiler,2014(6):47-50
［4］邓益忠.一台WNS10-1.25-Q燃气蒸汽锅炉前管板开裂原因分析［J］.工业锅炉，2011（6）:60-62
DENG YI-zhong. Cause analysis of front tube plate crack on reversal chamber of one WNS 10-1.25-Q steam boiler［J］. Industrial Boiler,2011(6):60-62
［5］吴恭平，赵吉鹏.某燃气锅炉管板裂纹原因及预防措施［J］.工业锅炉，2009(1)：54-58
WU Gong-ping,ZHAO Ji-peng.The cause and preventing of the tube plate crack of one gas-fired boiler［J］. Industrial Boiler,2009(1):54-58
［6］余笑枫.WNS燃气热水锅炉管口裂纹的原因及对策［J］，工业锅炉,2004(1):51-54
YU Xiao-feng.Analysis and solutions for cracks in pine ends of gas-fired hot water of WNS series［J］. Industrial Boiler,2004(1):51-54
［7］王迪.卧式内燃热水锅炉后管板发生裂纹的机理［J］，锅炉制造,2014(4):49-51
WANG Di.Horizontal internal combustion hot water boiler back tube plate crack mechanism［J］.Boiler Manufacturing,2014(4):49-51
［8］郭吉林，王建敏，周波.水火管工业锅炉烟管管端开裂有限元分析［J］.工业锅炉， 2011(6)：41-43
GUO Ji-lin，WANG Jian-min，ZHOU Bo.The finite element analysis of cracking in front tube of shell boiler［J］. Industrial Boiler,2011(6)：41-43
［10］王小平，吴恭平，赵吉鹏，王旭.WNS型热水锅炉管板裂纹原因分析及其设计优化［J］.工业锅炉，2009（3）:50-53
WANG Xiao-ping,WU Gong-ping,ZHAO Ji-peng,WANG Xu.The reasons of the tube-sheet crack and optimizing design of WNS hot water boilers［J］. Industrial Boiler，2009（3）:50-53
相似文献/References:
[1]徐洪华,田迎华.RBF神经网络在锅炉安全液位控制中的应用[J].中国安全生产科学技术,2011,7(8):170.
XU Hong-hua,TIAN Ying-hua.Safety level control of industrial boiler on RBFNN[J].JOURNAL OF SAFETY SCIENCE AND TECHNOLOGY,2011,7(9):170.
[2]陈红江,彭小兰.突变级数法在电站燃煤锅炉结渣预测中的应用[J].中国安全生产科学技术,2014,10(8):97.[doi:10.11731/j.issn.1673-193x.2014.08.017]
CHEN Hong-jiang,PENG Xiao-lan.Application of catastrophe progression method in forecasting slagging of coal-fired boiler[J].JOURNAL OF SAFETY SCIENCE AND TECHNOLOGY,2014,10(9):97.[doi:10.11731/j.issn.1673-193x.2014.08.017]
备注/Memo
- 备注/Memo:
- -