|本期目录/Table of Contents|

[1]袁征,吴小龙,雷正,等.深水井套管强度衰减规律及预防措施研究*[J].中国安全生产科学技术,2024,20(2):69-74.[doi:10.11731/j.issn.1673-193x.2024.02.009]
　YUAN Zheng,WU Xiaolong,LEI Zheng,et al.Study on strength attenuation law and preventive measures of cashing in deepwater wells[J].JOURNAL OF SAFETY SCIENCE AND TECHNOLOGY,2024,20(2):69-74.[doi:10.11731/j.issn.1673-193x.2024.02.009]
点击复制

深水井套管强度衰减规律及预防措施研究*
分享到：

《中国安全生产科学技术》[ISSN:1673-193X/CN:11-5335/TB]

卷:
20
期数:
2024年2期
页码:
69-74
栏目:
职业安全卫生管理与技术
出版日期:
2024-02-29

文章信息/Info

Title:
Study on strength attenuation law and preventive measures of cashing in deepwater wells
文章编号:
1673-193X(2024)-02-0069-06
作者:
袁征; 吴小龙; 雷正; 杨浩; 唐浩瑞; 张智; 邓皓匀
（1.中海油安全技术服务有限公司，海南 海口 570105;
2.西南石油大学 油气藏地质及开发工程国家重点实验室，四川 成都 610500）
Author(s):
YUAN Zheng;  WU Xiaolong;  LEI Zheng;  YANG Hao;  TANG Haorui;  ZHANG Zhi;  DENG Haoyun
(1.CNOOC Safety & Technology Services Co.,Ltd.,Haikou Hainan 570105,China;
2.State Key Laboratory of Oil and Gas Reservoir Geology and Exploitation，Southwest Petroleum University,Chengdu Sichuan 610500,China)
关键词:
深水套管; 强度衰减; 多因素; 强度校核; 预防措施
Keywords:
deepwater casing;  strength attenuation;  multi-factor;  strength check;  preventive measure
分类号:
X937
DOI:
10.11731/j.issn.1673-193x.2024.02.009
文献标志码:
A
摘要:
为研究深水井套管柱在多因素耦合作用下管柱完整性失效规律，综合考虑腐蚀、磨损以及温度共同作用，建立套管强度衰减评价方法，对比不同管材在多因素作用下强度衰减程度，提出降低套管强度衰减速率措施。研究结果表明：在腐蚀作用下，随着生产年限增加，套管强度衰减速率加快。腐蚀速率为1.0 mm/a时，P110套管抗内压强度平均每年下降7.21%；套管强度随磨损深度增加而减小。当磨损深度为0.3 mm时，L80、13Cr-P110和Q125 3种管材的抗外挤强度平均下降百分比为6.47%；管材强度一般随着温度升高而降低，当温度为100 ℃时，P110套管的抗内压强度下降6.37%；选用耐腐蚀、磨损和高温管材能够有效减小强度衰减速率。研究结果可为深水井开发提供参考。
Abstract:
In order to study the failure law of string integrity under multi-factor coupling effect in deepwater wells,comprehensively considering the joint effect of corrosion,wear and temperature,an evaluation method of casing strength attenuation was established.The strength attenuation degrees of different pipe materials under the action of multiple factors were compared,and the measures to reduce the strength attenuation rate of casing were proposed.The results show that under the action of corrosion,the strength attenuation rate of casing accelerates as the production life increases.When the corrosion rate is 1.0 mm/a,the internal pressure strength of P110 casing decreases by 7.21% per year on average.The strength of casing decreases as the wear depth increases.When the wear depth is 0.3 mm,the average reduction percentage of the external extrusion strength of L80,13Cr-P110 and Q125 pipe materials is 6.47%.The strength of pipe material generally decreases as the temperature increases.When the temperature is 100 ℃,the internal pressure strength of P110 casing decreases by 6.37%.The selection of corrosion-resistant,wear resistance and high-temperature resistance pipe materials can effectively reduce the strength attenuation rate.The research results can provide a reference for the development of deepwater wells.

参考文献/References:

［1］刘书杰,马传华,唐龙，等.南海深水高温高压气井最大环空压力允许值计算方法［J］.中国海上油气,2023,35(1):98-106. LIU Shujie,MA Chuanhua,TANG Long,et al.Calculation method of allowable maximum annulus pressure of deep water HTHP gas wells in South China sea［J］.China Offshore Oil and Gas,2023,35(1):98-106.
［2］中国能源报.深水领域成为全球油气勘探发现主战场［EB/OL］.（2022-10-17）［2023-09-01］http://paper.people.com.cn/zgnyb/html/2022-10/17/content_25944750.htm.
［3］程心平,薛德栋,张磊，等.南海深水井下采注技术挑战与对策［J］.科学技术与工程,2023,23(8):3123-3133. CHENG Xinping,XUE Dedong,ZHANG Lei,et al.Challenges and countermeasures of deep-water downhole productionand injection technology in the South China Sea［J］.Science Technology and Engineering,2023,23(8):3123-3133.
［4］黄灵刚,李广,周振宇，等.海上油田腐蚀套管更换实践［J］.石油钻采工艺,2012,34(增刊1):121-124. HUANG Linggang,LI Guang,ZHOU Zhenyu,et al.Change practice of the corroded casing pipes in offshore Oilfield［J］.Oil Drilling & Production Technology，2012,34(Supplement 1):121-124.
［5］PANDEY S K,RANA S A,FAKHROO A J.Wellstructure integrity threat due to near surface corrosion of outer casing at offshore wells［C］//IPTC 2014:International Petroleum Technology Conference.European Association of Geoscientists & Engineers,2014:IPTC-17557-MS.4
［6］曾春珉,韦龙贵,张超，等.南海西部油田高温高压气井套管磨损预测［J］.石油钻探技术,2015,43(6):46-53. ZENG Chunmin,WEI Longgui,ZHANG Chao,et al.Casing wear prediction for HTHP gas wells in west of South China Sea Oilfield［J］.Petroleum Drilling Techniques,2015,43(6):46-53.
［7］张智,孔维伟,刘志伟，等.腐蚀缺陷套管的剩余强度研究［J］.中国科技论文,2016,11(21):2467-2472. ZHANG Zhi,KONG Weiwei,LIU Zhiwei,et al.Study on residual strength of corrosion defect casing［J］.China Sciencepaper,2016,11(21):2467-2472.
［8］张强,练章华,林铁军,等.气体钻与泥浆钻全井段套管磨损对比研究［J］.中国安全生产科学技术,2018,14(6):121-127. ZHANG Qiang,LIAN Zhanghua,LIN Tiejun,et al.Comparative study on casing wear of whole well section by gas drilling and mud drilling［J］.Journal of Safety Science and Technology,2018,14(6):121-127.
［9］周传喜,田海锋,郭伟，等.井筒温度对含缺陷套管抗挤强度的影响［J］.石油机械,2022,50(10):142-148. ZHOU Chuanxi,TIAN Haifeng,GUO Wei,et al.Influence of wellbore temperature on collapsing strength of defective casing［J］.China Petroleum Machinery,2022,50(10):142-148.
［10］席岩,柳贡慧,李军，等.页岩气井体积压裂井筒温度计算及套管强度变化分析［J］.断块油气田,2017,24(4):561-564. XI Yan,LIU Gonghui,LI Jun,et al.Calculation of wellbore temperature and analysis of its effect on casing strength during volume fracturing in shale gas well［J］.Fault-Block Oil & Gas Field,2017,24(4):561-564.
［11］黄文君,张星坤,高德利.复合磨损模式下的套管失效风险预测方法——以φ193.68 mm×12.7 mm套管为例［J］.天然气工业,2022,42(7):85-94. HUANG Wenjun,ZHANG Xingkun,GAO Deli.Prediction method of casing failure risk under compound wear mode:a case study on φ193.68 mm×12.7 mm casing［J］.Natural Gas Industry,2022,42(7):85-94.
［12］张智,蔡楠,赵苑瑾，等.四川盆地超深高含硫气田井下管柱完整性设计理念与方法［J］.天然气工业,2023,43(4):148-156. ZHANG Zhi,CAI Nan,ZHAO Yuanjin,et al.Downhole string integrity design for ultra-deep high-sulfur gas fields in the Sichuan basin:concept and methodology［J］.Natural Gas Industry,2023,43(4):148-156.
［13］幸雪松,武治强,张星坤，等.复合月牙形磨损套管剩余强度研究［J］.石油机械,2022,50(11):126-132. XING Xuesong,WU Zhiqiang,ZHANG Xingkun,et al.Study on residual strength of composite crescent worn casing［J］.China Petroleum Machinery,2022,50(11):126-132.
［14］API.Technical report on equations and calculations for casing,tubing,and line pipe used as casing or tubing;and performance properties tables for casing and tubing:API 2008［S］.Washington DC:API,2008.
［15］陈力力,李玉飞,张智，等.水平井套管磨损规律及防磨优化研究［J］.钻采工艺,2022,45(2):21-27. CHEN Lili,LI Yufei,ZHANG Zhi,et al.Casing wear law and anti-wear optimization in horizontal wells［J］.Drilling & Production Technology,2022,45(2):21-27.
［16］张智.深井高温高压条件下套管柱强度设计方法及计算机软件研究［D］.成都:西南石油大学,2003.
［17］刘小刚,陶林,王玉山，等.渤海油田高温高压井套管优化设计［J］.断块油气田,2011,18(6):787-789. LIU Xiaogang,TAO Lin,WANG Yushan,et al.Optimal design of casing of high temperature and high pressure well in Bohai Oilfield［J］.Fault-Block Oil & Gas Field,2011,18(6):787-789.
［18］ZHANG Z,DING J,ZHENG Y,et al.Mechanical integrity of tubing string in high-temperature and high-pressure ultra-deep gas wells based on uncertainty theory［J］.Energy Science & Engineering,2022,10(7):2106-2122.
［19］ISO.Petroleum and natural gas industries：formulae and calculation for casing,tubing,drill pipe and line properties:ISO 10400［S］.Geneva:ISO,2007.

相似文献/References:

备注/Memo

备注/Memo:
收稿日期： 2023-09-19
* 基金项目： 中海油能源发展股份有限公司安全环保分公司科研专项项目（HFKJ-STS2022-03）
作者简介： 袁征，硕士，工程师，主要研究方向为海上油气田安全技术与管理。
更新日期/Last Update: 2024-03-11